 產品詳細介紹 |
|
項 目 \ 牌 號 |
特種高鋁磚 |
硅線石磚
|
紅柱石磚
|
高鋁堇青石磚
|
|
SAL40S |
SAL40P |
SAL40 |
SAL39S |
SAL39 |
SAL38 |
SAL37 |
SAL36 |
LS-65 |
LS-60 |
HS-60 |
HS-55 |
SPCD-50 |
SPCD-60 |
Al2O3 %
|
≥92
|
≥90
|
≥85
|
≥80
|
≥75
|
≥70
|
≥60
|
≥50
|
≥65
|
≥60
|
≥60
|
≥55
|
≥50 |
≥60 |
| Fe2O3 % |
≤0.8
|
≤0.8
|
≤1.0
|
≤1.2 |
≤1.2
|
≤1.5
|
≤1.5
|
≤1.5
|
|
|
|
|
|
|
| 耐火度 ℃ |
≥1850
|
≥1850
|
≥1850
|
|
≥1820
|
≥1850
|
≥1820
|
≥1790
|
≥1790
|
≥1790
|
≥1790
|
≥1770
|
≥1770
|
≥1790
|
| 顯氣孔率 % |
≤18
|
≤19
|
≤19
|
≤20
|
≤20
|
≤20
|
≤20
|
≤20
|
≤22 |
≤22 |
≤22 |
≤22 |
≤24 |
≤24 |
| 體積密度(參考) g/cm3 |
≥3.0
|
≥2.90
|
≥2.85
|
≥2.8
|
≥2.7
|
≥2.6
|
≥2.46
|
≥2.36
|
|
|
|
|
|
|
| 常溫耐壓強度 MPa |
≥80
|
≥70
|
≥70
|
≥70
|
≥60
|
≥55
|
≥45
|
≥40
|
≥50
|
≥50
|
≥40
|
≥40
|
≥40
|
≥50
|
| 荷重軟化溫度 T2 ℃ |
≥1700
|
≥1700
|
≥1700
|
≥1650
|
≥1650 |
≥1600 |
≥1550 |
≥1500 |
≥1550
|
≥1500
|
≥1500
|
≥1450
|
|
|
重燒線
變化率 %
|
1600℃×2h |
±0.1 |
±0.1 |
±0.1 |
0-+0.5 |
|
|
|
|
|
|
|
|
|
|
| 1500℃×2h |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 1400℃
0-+0.5 ×3h |
|
|
|
|
|
|
|
|
±0.2 |
±0.2 |
±0.2 |
±0.2 |
|
|
| 1000℃ 線膨脹率 % |
≤0.8 |
≤0.8 |
≤0.75 |
|
≤0.7 |
≤0.7 |
≤0.65 |
≤0.6 |
|
|
|
|
≤+0.5 |
≤+0.5 |
Thermal 熱震穩定性,次
(1100℃ 水冷) |
|
|
|
|
|
|
|
|
≥20 |
≥20 |
≥20 |
≥20 |
≥12 |
≥12 |
| 用 途 |
各種工業窯爐及熱工設備內襯等。
|
用于溫度變化劇烈的工業窯爐
及熱工設備內襯
|
各種工業窯爐的燒
嘴磚及陶瓷窯具磚
| |
|
Item項 目 \ Brand牌 號 |
Special High-Alumian Bricks特種高鋁磚 |
|
H2 |
H2S |
H3 |
H3S |
HAL60 |
HAL70 |
HAL75 |
HAL80 |
HA80E |
HA80HE |
HA70HE |
HA65E |
K65 |
K70 |
Al2O3 %
|
≥60
|
≥63
|
≥50
|
≥52
|
≥60
|
≥70
|
≥75
|
≥80
|
≥80
|
≥78
|
≥70
|
≥65
|
≥65
|
≥68
|
| Fe2O3 % |
≤1.8
|
≤1.8
|
≤2
|
≤1.7
|
≤1.5
|
≤1.7
|
≤2
|
≤1.8
|
≤1.8
|
≤1.5
|
≤1.8
|
≤2
|
≤1.5
|
≤1.8
|
| 耐火度 SKRefractoriness |
≥36
|
≥36
|
≥36
|
≥36
|
≥36
|
≥37
|
≥37
|
≥37
|
≥37
|
≥37
|
≥37
|
|
|
|
| 顯氣孔率 %Apparent Porosity |
≤21
|
≤21
|
≤21
|
≤20
|
≤21
|
≤21
|
≤20
|
≤20
|
≤20
|
≤19
|
≤19
|
≤22
|
≤20
|
≤21
|
| 體積密度(參考) g/cm3Bulk Density |
≥2.4
|
≥2.45
|
≥2.30
|
≥2.35
|
≥2.40
|
≥2.6
|
≥2.65
|
≥2.7
|
≥2.6
|
≥2.7
|
≥2.7
|
≥2.4
|
≥2.5
|
≥2.55
|
| 常溫耐壓強度 MPaCold crushing strength |
≥45
|
≥50
|
≥40
|
≥45
|
≥40
|
≥50
|
≥60
|
≥60
|
≥60
|
≥70
|
≥80
|
≥50
|
≥55
|
≥50
|
| Refractoriness under Load荷重軟化溫度 T2 ℃ |
≥1520 |
≥1520 |
≥1450 |
≥1470 |
≥1530 |
≥1550 |
≥1550 |
≥1550 |
≥1540 |
≥1600 |
≥1550 |
≥1500 |
≥1550 |
≥1500 |
重燒線
變化率 %
Permanent
Linear Change |
1600℃×2h |
|
|
|
|
|
|
|
|
|
0～+4 |
0～+4 |
|
|
2～5 |
| 1500℃×2h |
0～+1 |
0～+1 |
-0.1～+0.5 |
0～+1 |
|
0～+2 |
0～+0.5 |
0～+1 |
0～+0.5 |
|
|
0～+1 |
0～+1 |
| | | | |
|